VTS20014 UV-cure roller filler (catalog: clear universal UV filler-primer)
Mix calculator
Ask about VTS20014
Answers are based on the VTS20014 data and the products it mixes with.
Mixing matrix
- Thinner% by weight: 0 %recommended% by volume: 0 %recommended
Standard — use as supplied
It is 100 % solids: adding solvent hurts the cure and causes pinholes/bubbles.
- % by weight: 0–3 %recommended% by volume: 0–4 %recommended
Only if the material is too heavy for the rollers in a cold shop
Warming the material to 22–25 °C is better than thinning. If thinned, flash off before the lamps.
| Role | Material | % by weight | % by volume | When |
|---|---|---|---|---|
| Thinner | 0 %recommended | 0 %recommended | Standard — use as suppliedIt is 100 % solids: adding solvent hurts the cure and causes pinholes/bubbles. | |
| Thinner | S30 / S31 | 0–3 %recommended | 0–4 %recommended | Only if the material is too heavy for the rollers in a cold shopWarming the material to 22–25 °C is better than thinning. If thinned, flash off before the lamps. |
Percentages are per 100 parts of component A.
Characteristics
- Solids
- 100catalog
- Adhesion and wetting
- good wetting and adhesion to various substratesofficial
- Sanding
- easy to sandcatalog
- Pore filling
- goodcatalog
- Pot life
- n/a — 1K UV-cure, no hardener; stays workable in the trough until exposed to UVrecommended
- Drying · Cure
- UV lamp, start at 1 lamp 80–120 W/cm, 10 m/min (gel cure, sandable/overcoatable straight off the line)recommended
- Drying · Conditions
- UV cure; ambient 18–25 °C typical
Colours
- clear · clear
Application
Roller coater (UV)
- Consumption
- 30–35 g/m²official
- Wet film
- 25–33 µmrecommended
- Coats
- 1–2 passes (filler roller, often reverse/smoothing roller after)recommended
- Flash-off
- 0recommended
- Recoat
- immediately after UV gel cure (1 lamp 80–120 W/cm, 10 m/min), then UV primers 20–25 g/m²recommended
- Sanding between coats
- normally no sanding after the filler; sand after the primer build, P240–P320 (as in the UV schedules)recommended
- Nozzle
- n/a — roller-only product, not for sprayingrecommended
Filler (doctor/applicator) roller + reverse/smoothing roller on flat parts; cure in-line immediately.
Process and compatibility
- Substrate preparation
- Sand P150–P180–P220; if staining, CPS stain 60–80 g/m², dry 20–25 °C 5 min (anegri UV schedule) — or VTS20000 sealer 8–10 g/m², dry 30–35 °C 5 min (parquet UV schedule) — before the fillerschedule
- Goes over
- bare wood/veneer / CPS stain mixes (schedule analogue) / VTS20000 (parquet sealer, schedule analogue)
- Sanding
- No intermediate sanding needed after filler; sand the cured primer build P240–P320recommended
- Temperature and humidity
- Material and parts 18–25 °C, RH 50–70 %; wood MC 8–10 %recommended
- Don'ts
- Do not spray — roller only
- Do not leave the trough in sunlight/UV
- Do not thin unless you have to
- Not for profiled parts
Storage
- Storage temperature
- Store in closed opaque container away from light, 5–30 °Crecommended
Safety: UV acrylates are skin sensitisers: nitrile gloves, eye protection; shield eyes from lamp radiation.
Sources
Value tags: “official”, “dealer”, “catalog”, “schedule” are Technocolor data; “workshop” is from our own datasheets; “recommended” is our engineering estimate (hover to see the reasoning).
- official page: properties, roller 30–35 g/m²
- roller method: 98–100 % solids UV, flat parts only
- UV parquet schedule (VTS20011 analogue, lamp «80–120 Вт» 1/3 lamps 10 m/min)
- UV anegri veneer schedule (VTS20011 analogue)
- dealer search — no result
Not covered by the sources
- dealer page: VTS20014 not found by t-colormarket.ru search (re-checked 2026-10-05) nor on lakokraska31/woodonline/ndom31
- no TDS found (web search budget exhausted)
- viscosity, density, gloss, hardness, chemical resistance — unpublished
- UV cure dose/lamp settings specific to VTS20014 (derived from VTS20011 schedule)
- shelf life and packaging
- not used in any official finishing schedule
- lamp unit: schedules print «80–120 Вт» without /cm; W/cm assumed
- VTS20014 is absent from the 2025-2026 catalog transcripts (only in the older Katalog-Technocolor_web.pdf) — may be discontinued