CIT solvent stain → 2× PE (unsaturated polyester, peroxide/accelerator cure) clear primer → 2K PU thixotropic 100-gloss topcoat
Solid-oak coffin finishing (clear high-gloss polyester / PU)
- Substrate
- Solid oak (coffins and funeral caskets), open-pored wood
- Result
- Clear, stained, high-gloss (about 100 GU) closed-pore finish with a thick 'lens'. The thixotropic topcoat does not sag on the coffin's vertical sides.
- 01
Hand sanding
Abrasive: P150, P180
Solid-wood prep: P150, then P180. Blow the dust out of the pores before staining.
- 02
Staining, automatic spraying
CITS10 (Thinner)
- Nozzle · Value
- 1.0–1.3 mm (air/HVLP-type auto gun)
- Nozzle · Why ru
- В схеме не указано. Морилка очень жидкая (разбавление 5–20×) и наносится автоматическим пистолетом по 80–100 г/м² — обычная практика для сольвентных морилок.
- Pressure · Value
- 2–3 bar atomising air
- Pressure · Why ru
- Обычное пневматическое распыление для маловязких морилок (information__methods: пневматическое распыление).
- Consumption
- 80-100
80–100 g/m² matches the official CIT page. According to the product page the stain is lightfast and transparent and does not raise the grain, so there is no sanding between coats.
- 03
Drying in a drying chamber
Drying: 20 °C, 5-10 min
Lets the stain solvent flash off before the PE primer.
- 04
Priming coat 1, automatic spraying
ETS50 100 %EC1 2 % (Catalyst)EA1 2 % (Accelerator)S10 / S11 15 % (Thinner)
- Nozzle · Value
- 0.28–0.33 mm (tip 011–013)
- Nozzle · Why ru
- В схеме не указано. Airless работает при давлении до 200 бар (information__methods). Высоконаполненный полиэфирный грунт вязкостью около 12 с по VZ-8 (дилер, ETS20) при 250 г/м² обычно наносят соплом 0,011–0,013″ с углом факела 40–50°.
- Pressure · Value
- 120–160
- Pressure · Why ru
- В схеме не указано. Airless работает при давлении до 200 бар (information__methods). Высоконаполненный полиэфирный грунт вязкостью около 12 с по VZ-8 (дилер, ETS20) при 250 г/м² обычно наносят соплом 0,011–0,013″ с углом факела 40–50°.
- Consumption
- 250
'Airless with 2 intakes': in PE systems the peroxide (EC1) and the accelerator (EA1) must never be mixed directly with each other, and a mix with both gels fast (ETS20 pot life is about 20 min). So the material is made up in two containers, ETS50 + EC1 and ETS50 + EA1. The pump draws them 1:1 and they only meet in the gun. 250 g/m² is the top of the ETS20 range (200–250 g/m²): oak's open pores need a thick filling coat.
Mix for this step
- 05
Drying in a drying chamber
Drying: 20 °C, 30-40 min
Flash/gel time between coats. ETS20 is touch-dry in about 40 min (dealer). The second PE coat goes on without sanding.
- 06
Priming coat 2, automatic spraying
ETS50 100 %EC1 2 % (Catalyst)EA1 2 % (Accelerator)S10 / S11 15 % (Thinner)
- Nozzle · Value
- 0.28–0.33 mm (tip 011–013)
- Nozzle · Why ru
- В схеме не указано. Airless работает при давлении до 200 бар (information__methods). Высоконаполненный полиэфирный грунт вязкостью около 12 с по VZ-8 (дилер, ETS20) при 250 г/м² обычно наносят соплом 0,011–0,013″ с углом факела 40–50°.
- Pressure · Value
- 120–160
- Pressure · Why ru
- В схеме не указано. Airless работает при давлении до 200 бар (information__methods). Высоконаполненный полиэфирный грунт вязкостью около 12 с по VZ-8 (дилер, ETS20) при 250 г/м² обычно наносят соплом 0,011–0,013″ с углом факела 40–50°.
- Consumption
- 250
This is the second step numbered '5' in the official table. Same recipe as step 4. About 500 g/m² of PE in total fills the oak pores.
Mix for this step
- 07
Drying on racks / in a drying chamber
Drying: 20 °C, 8-12 h
Cure until sandable. The dealer gives 12 h to sanding at 20 °C for ETS20.
- 08
Hand sanding
Abrasive: P360, P400
Levels the PE film for gloss. Scuffing also gives the PU topcoat something to grip (information__characteristics, 'Adhesion'). Do not cut through to the stain on edges.
- 09
Topcoat, automatic spraying
PTL500 100 %C200 70 % (Hardener)S80 40 % (Thinner)
- Nozzle · Value
- 0.23–0.28 mm (tip 009–011, fine-finish)
- Nozzle · Why ru
- В схеме не указано. 2К ПУ с разбавлением при 150 г/м² — это тонкая финишная работа. Для финишных слоёв airless стандартно берут сопла меньше, чем для ПЭ грунта; Airmix с теми же соплами дал бы лучшую поверхность (information__methods).
- Pressure · Value
- 80–120
- Pressure · Why ru
- Ниже, чем для грунта, чтобы ограничить шагрень на тиксотропном глянцевом слое (information__characteristics: тиксотропные покрытия хуже растекаются).
- Consumption
- 150
The thixotropic lacquer does not sag on vertical sides. The dealer names coffins among PTL500's uses. 150 g/m² matches the official page. Mix pot life is 4 h (dealer).
Mix for this step
Mix calculator
gRatio 100 : 70.0 : 40.0
Component Weigh out PTL500part A 238 g C200Hardener 167 g S80Thinner 95.2 g Total 500 g Covers roughly 3.33 m² at 150 g/m².
Pot life of the mix: 4.
- 10
Drying in a drying chamber
Drying: 20 °C, 8-12 h
PTL500 is touch-dry in 1 h and fully dry in 12 h (dealer). The schedule has no polishing step. PTL500 'polishes very well' (dealer), so polishing, if needed, comes after full cure.
Ask about this system
Answers are based on this finishing schedule and its products.
System characteristics
- Gloss · Value
- ≈100 GU (high gloss, measured at 20° geometry)
- Gloss · Why ru
- На официальной странице PTL500 — «High gloss»; дилер указывает уровень блеска «100 Gloss». information__characteristics: геометрия 20° — для зеркально-глянцевых поверхностей.
- Dry solids · Value · ETS20 part A (proxy)
- 92 ±1 % (dealer) / 96 % (catalogue 2025)
- Dry solids · Value · PTL500 part A
- 56 ±1 % (dealer)
- Dry solids · Value · AC200
- 44 ±1 % (dealer)
- Dry solids · Value · EC1
- 100 ±1 % (dealer)
- Dry solids · Why ru
- t-colormarket.ru, «Все технические характеристики». Значение для ETS50 взято от ETS20, так как по ETS50 данных нет.
- Total build · Value
- ≈ 0.30–0.35 mm dry (≈ 2×160 µm PE − 20–40 µm sanded off + ≈ 50 µm PU)
- Total build · Why ru
- ПЭ смесь 100+2+2+15: нелетучие ≈ (92+2+~1)/119 ≈ 80 % → 250 г/м² мокрого ≈ 200 г/м² сухого ≈ 160–170 мкм при ~1,2 г/см³ за слой. Смесь PTL500 100+70+40: (56+0,44×70)/210 ≈ 41 % → 150 г/м² ≈ 62 г/м² ≈ 50–55 мкм. information__characteristics: высоконаполненные грунты за один проход дают толстую закрытопористую плёнку.
- Pore filling · Value
- closed-pore finish
- Pore filling · Why ru
- Около 500 г/м² PE с высоким сухим остатком по дубу плюс выравнивание P360/P400 — классический закрытопористый набор слоя. Официальные свойства ETS20 — минимальная усадка и хорошая шлифуемость.
- Hardness · Value
- high (PE base very hard; PU topcoat good hardness and scratch resistance)
- Hardness · Why ru
- Дилер: ETS20 — «высокий сухой остаток и твёрдость»; PTL500 — «хорошая твёрдость и стойкость к царапинам». В information__characteristics предупреждается, что твёрдые покрытия в толстом слое хрупкие, — это важно для ПЭ-слоя ~0,3 мм.
- Elasticity · Value
- low–moderate; risk of cracking if the wood moves
- Elasticity · Why ru
- Толстый жёсткий ПЭ по массиву дуба. information__characteristics («Эластичность»): при переносе изделия в другие климатические условия меняются размеры; гроб — не изделие длительной эксплуатации, поэтому риск приемлем.
- Chemical resistance · Value
- good
- Chemical resistance · Why ru
- Для PTL500/ETS50 цифр нет. Каталог 2025 оценивает линейку PE (ETL200) как имеющую «отличную физико-химическую стойкость», а 2К ПУ-глянцевые покрытия с AC200 позиционируются для кухонной мебели и мебели для ванных (текст каталога PPL200/ATL500). Гробы химическому воздействию не подвергаются.
- Light resistance · Value
- stain: good; system: moderate (some yellowing of PE/PU over time possible)
- Light resistance · Why ru
- Официально у CIT: «хорошая светостойкость». Тип изоцианата AC200 (алифатический/ароматический) не опубликован; в information__characteristics сказано, что светостойкость ПУ зависит от изоцианата отвердителя. ПЭ также склонен желтеть под УФ.
- Thixotropy · Value
- topcoat thixotropic, no sagging on vertical surfaces
- Thixotropy · Why ru
- Официально по PTL500: «Высокоглянцевый, тиксотропный»; дилер: «отличная стойкость к потёкам… для вертикальных изделий».
- Viscosity · Value · ETS20 part A (proxy)
- 12 ±2 s VZ-8
- Viscosity · Value · PTL500 part A
- 60 ±5 s VZ-4
- Viscosity · Why ru
- Технические характеристики t-colormarket.ru (измерение вискозиметром типа Ford, см. information__characteristics «Вязкость»).
- Pot life · Value · PE primer (ETS20 proxy)
- 20 min / 1.5 h (dealer, two figures as published, likely the full catalysed mix / the half-mixes for the 2-intake system)
- Pot life · Value · PTL500 with AC200
- 4 h
- Pot life · Why ru
- t-colormarket.ru: «Жизнеспособность катализированного продукта (при 20 °C)».
- Drying times · Value · ETS20 touch dry
- 40 min
- Drying times · Value · ETS20 sanding
- 12 h
- Drying times · Value · PTL500 touch dry
- 1 h
- Drying times · Value · PTL500 full cure
- 12 h
- Drying times · Why ru
- Технические характеристики t-colormarket.ru при 20 °C; согласуется со стадиями сушки 8–12 ч в схеме.
- Adhesion · Value
- intercoat adhesion relies on the P360/P400 sanding of the cured PE
- Adhesion · Why ru
- information__characteristics: межслойная адгезия важна при разной химии грунта и финиша и улучшается с шероховатостью поверхности.
- Coats
- 4
- Coats breakdown · Stain
- 1
- Coats breakdown · PE primer
- 2
- Coats breakdown · PU topcoat
- 1
- Wet consumption (g/m²)
- 730-750
- Min cycle time (h)
- 16.6
- Max cycle time (h)
- 24.8