PTL200 A
PTL200 A PU gloss lacquer (100 gloss)
Two-pack gloss polyurethane lacquer (100 gloss) with good gloss, excellent flow and hardness. Lower solids and higher part-A viscosity than PTL200; cured with AC200 at 70 %, thinned with S70. No official page — dealer only.
- interior doors
- kitchen fronts
- tables
- chairs
Mix calculator
Ask about PTL200 A
Answers are based on the PTL200 A data and the products it mixes with.
Mixing matrix
- AC200Hardener% by weight: 70 %dealer% by volume: 70 %dealer
only published ratio
- S70Thinner% by weight: 30 %dealer% by volume: 35 %dealer
only published ratio
Stir thoroughly before use.
- S80Thinner% by weight: 30 %recommended
in heat (>25 °C), instead of S70
| Role | Material | % by weight | % by volume | When |
|---|---|---|---|---|
| Hardener | AC200 | 70 %dealer | 70 %dealer | only published ratio |
| Thinner | S70 | 30 %dealer | 35 %dealer | only published ratioStir thoroughly before use. |
| Thinner | S80 | 30 %recommended | — | in heat (>25 °C), instead of S70 |
Percentages are per 100 parts of component A.
Characteristics
- Solids
- 44 ± 1 %dealer
- Viscosity
- 55 ± 5 sdealer
- Density · Mixed
- 1 g/mlrecommended
- Gloss
- 100 GUdealer
- Pot life
- 6dealer
- Drying · Touch-dry
- 60dealer
- Drying · Full cure
- 12dealer
- Drying · Dust-free
- 20–30 minrecommended
- Drying · Sand or stack
- 12–24 hrecommended
- Drying · Conditions
- 20 °C
- Hardness
- good hardnessdealer
- Flow
- excellent flow-outdealer
Application
HVLP
- Nozzle
- 1.3–1.5 (typ. 1.4) mmrecommended
- Pressure · air
- 2–2.5 barrecommended
- Spray viscosity
- 16–20 s DIN4 / VZ-4recommended
- Consumption
- 120–150 g/m²dealer
- Wet film
- 120–150 µmrecommended
- Coats
- 1–2 coatsrecommended
- Flash-off
- 20–40 minrecommended
- Recoat
- after ≥12 h full dry, sanded; or wet-on-wet within ~1 hrecommended
- Sanding between coats
- P400–P600 (wet or with soft pad) before a second gloss coatrecommended
- Gun setup
- fan fully open, distance 15–20 cm, overlap 50–75 %, full wet passrecommended
Lay down a full wet coat — dry spray on a 100-gloss finish shows as orange peel. In hot weather add S100/S101 retarder at 5–10 % on top of the main thinner (dealer note).
Conventional spray
- Nozzle
- 1.4–1.6 (typ. 1.5) mmrecommended
- Pressure · air
- 3–4 barrecommended
- Spray viscosity
- 16–20 s DIN4 / VZ-4recommended
- Consumption
- 120–150 g/m²dealer
Transfer efficiency up to 40 % per the official methods page, so actual usage is higher than the nominal g/m².
Airmix (air-assisted airless)
- Nozzle
- 0.23–0.28 mmrecommended
- Pressure · fluid
- 20 barofficial
- Pressure · air
- 1–2 barofficial
- Spray viscosity
- 20–25 s DIN4 / VZ-4recommended
The official methods page names Airmix as better suited to topcoats than Airless.
Electrostatic
Usable with any gun type per the official methods page; settings follow the underlying method. Resistivity of the thinned material is not published — test before relying on electrostatics.
Process and compatibility
- Substrate preparation
- Flat, fully sanded primer (PU or polyester), final sand P320–P400 plus pads, de-dust and tack-rag.recommended
- Goes over
- EPS20
- Sanding · Before
- P320–P400 on primerrecommended
- Sanding · Between coats
- P400–P600recommended
- Sanding · Polishing
- not earlier than 3 days after final coatrecommended
- Temperature and humidity · Application
- 18–25 °Crecommended
- Temperature and humidity · Forced drying
- 30–35 °C for 30 min, then 72 h at 20–25 °C before polishingschedule
- Don'ts
- don't spray over an unsanded or dusty primer — a 100-gloss film shows every speck
- don't polish earlier than 3 days after the final coat (figure published for PTL200)
- don't exceed the recommended film (120–150 g/m² per coat) — dealer note
- don't use the mix past its 6 h pot life
- don't thin with fast thinners — the slow S70 is what lets it flow out
Storage
- Packaging
- 1 L,5 L,25 Ldealer
Safety: Two-pack solvent-borne polyurethane; the hardener contains isocyanates. Spray only in a ventilated booth wearing an A2P3 respirator (or air-fed mask), gloves and eye protection. Flammable — keep away from flames and sparks. (Generic 2K PU guidance; no Technocolor SDS was found.)
Mixed into
Sources
Value tags: “official”, “dealer”, “catalog”, “schedule” are Technocolor data; “workshop” is from our own datasheets; “recommended” is our engineering estimate (hover to see the reasoning).
- dealer: description, use, 120–150 g/m², AC200 70/70, S70 30 wt/35 vol, full technical characteristics, notes
- official application methods
- closest official gloss PU schedule (PPL200 with C200/S80)
Not covered by the sources
- no official t-color.ru page; not in the 2025-26 catalogue transcript
- relationship to PTL200 (new formulation vs. variant) not stated
- S80/PC210 compatibility not published for PTL200 A
- shelf life, storage temperature, density not published
- dust-free/sanding/polishing times, hardness value, chemical resistance not published
- no TDS/SDS PDF found